COMPARATIVE TESTS between silicon adhesives and non-silicone adhesives applied with the GEAR System – SIL method
indicate a greater tenacity of adhesion on silicon, for the adhesives applied with the GEAR System-SIL method, compared to the standard silicone adhesives applied with the traditional pressure method
TENACITY INCREASE with GEAR System-SIL method
from +47% to +91% depending on the type of adhesive
T-Pell ASTM 1876-01 N/10mm GIMATECH laboratory test
silicone gasket bonded with silicone adhesive applied with traditional method Fmean 5,415 N10/10mm Reference value for comparison of next tests with GEAR System – SIL method
T-Pell ASTM 1876-01 N/10mm GIMATECH laboratory test
silicone gasket bonded with ACRYLIC NON WOVEN TISSUE SUPPORT ADHESIVE (GEAR System –SIL method) Adhesion + 91,14 % greater than silicone adhesive applied with traditional method
T-Pell ASTM 1876-01 N/10mm GIMATECH laboratory test
silicone gasket bonded with MODIFIED ACRYLIC ADHESIVE (GEAR System –SIL method) Adhesion + 50,42% greater than silicone adhesive applied with traditional method
T-Pell ASTM 1876-01 N/10mm GIMATECH laboratory test
silicone gasket bonded with ACRYLIC NON SUPPORTED ADHESIVE (GEAR System –SIL method) Adhesion + 47,77% greater than silicone adhesive applied with traditional method
T-Pell ASTM 1876-01 N/10mm GIMATECH laboratory test
silicone gasket bonded with ACRYLIC FOAM ADHESIVE (GEAR System –SIL method) Adhesion + 89,29 % greater than silicone adhesive applied with traditional method
T-Pell ASTM 1876-01 N/10mm GIMATECH laboratory test
silicone gasket bonded with HOT MELT RUBBER ADHESIVE (GEAR System –SIL method) Adhesion + 49,55% greater than silicone adhesive applied with traditional method
Test method :
test: “T Peel Adhesion ASTM D 1876-01” on silicone rubber samples after 14 days from coupling with 7 different types of adhesives
sample: silicone rubber hardness 70 shore A, section 12×3 mm.
tested adhesive types: silicone – rubber based – modified acrylic – acrylic foam
adhesive height: 10 mm.
elapsed time between adhesivization and testing: 14 days
Compared results to conventional silicone adhesives applied with traditional method:
Increase in detachment resistance according to the types of adhesive tested (applied with GEAR System-SIL method):
– modified acrylic adhesive not supported (pure adhesive)
thermal resistance 82/121° C increased tenacity +47.77%
– modified acrylic adhesive with non-woven support
thermal resistance 90/120° C increased tenacity +91.14%
– modified acrylic adhesive with polyester support
thermal resistance 185° C tenacity increase +50.42%
– structural acrylic foam adhesive
thermal resistance 93/150° C increased tenacity +89.29%
– non-supported reticulated rubber based adhesive
thermal resistance 65/75° C increase in strength +49.55%